Silver brazing solder 6250 |
Physico-
chemical Data |
Type of
brazing alloy |
Area of brazing |
Base metal |
Flux
|
Brazing process |
Brazing alloy
composition
|
Ag: 24 – 26 %
Cu: 39 – 41 %
Zn: 33 – 37 % |
DIN 8513:
L-Ag25
EN 1044:
AG 205
|
Brazing joints with temperature stress up to 200 °C
Gap soldering
Braze welding
|
Steel
Copper
Copper alloys
Nickel
Nickel alloys
|
V87
KMB-S 62
Oktol 88
Flux "S"
SFP
891
|
Oxyfuel torch brazing
Furnace brazing
Induction brazing
Laser brazing
ABA-FAG-process |
Tensils strength of2 the brazing joint |
about
380 N/mm2 |
Melting range |
700 – 790 °C |
Brazing temperature |
780 °C |
|
|
Silver brazing solder 6440 |
Physico-
chemical Data |
Type of
brazing alloy |
Area of brazing |
Base metal |
Flux |
Brazing process |
Welding alloy composition
|
Ag: 43 – 45 %
Cu: 29 – 31 %
Zn: 24 – 28 % |
DIN 8513:
L-Ag44
EN 1044:
AG 203 |
Brazing joints with temperature stress up to 200 °C
Gap soldering
Braze welding
|
Steel
Copper
Copper alloys
Nickel
Nickel alloys
|
SFP 89
SFP 891
Flux "S"
|
Oxyfuel torch brazing
Furnace brazing
Induction brazing
Laser brazing
ABA-FAG-process |
Tensils strength of2 the brazing joint |
about
400 N/mm2 |
Melting range |
675 – 735 °C |
Brazing temperature |
730 °C |
|
|
Silver brazing solder 6201 |
Physico-
chemical Data |
Type of
brazing alloy |
Area of brazing |
Base metal |
Flux |
Brazing process |
Welding alloy composition |
Ag: 19 – 21 %
Cu: 39 – 41 %
Cd: 13 – 17 %
Zn: 23 – 27 % |
DIN 8513:
L-Ag20Cd
EN 1044:
AG 309 |
Brazing joints with temperature stress up to 150 °C
Gap soldering
Braze welding
|
Steel
Copper
Copper alloys
Nickel
Nickel alloys
|
V87
KMB-S 62
Oktol 88
SFP 891
Flux "S"
SFP 89
|
Oxyfuel torch brazing
Furnace brazing
Induction brazing
ABA-FAG-process
|
Tensils strength of2 the brazing joint
|
about
350 N/mm2 |
Melting range |
605 – 765 °C |
Brazing temperature |
750 °C |
|
|
Silver brazing solder 6301 |
Physico-
chemical Data |
Type of
brazing alloy |
Area of brazing |
Base metal |
Flux |
Brazing process |
Welding alloy composition |
Ag: 29 – 31 %
Cu: 27 – 29 %
Cd: 19 – 23 %
Zn: 19 – 23 % |
DIN 8513:
L-Ag30Cd
EN 1044:
AG 306
|
Brazing joints with temperature stress up to 150 °C
Gap soldering
Braze welding
|
Steel
Stainless steel
Copper
Copper alloys
Nickel
Nickel alloys
|
SFP 89
SFP 891
Flux "S"
|
Oxyfuel torch brazing
Furnace brazing
Induction brazing
ABA-FAG-process
|
Tensils strength of2 the brazing joint |
about
380 N/mm2 |
Melting range |
600 – 690 °C |
Brazing temperature |
680 °C |
|
|
Silver brazing solder 6401 |
Physico-
chemical Data |
Type of
brazing alloy |
Area of brazing |
Base metal |
Flux |
Brazing process |
Welding alloy composition |
Ag: 39 – 41 %
Cu: 18 – 20 %
Cd: 18 – 22 %
Zn: 19 – 23 % |
DIN 8513:
L-Ag40Cd
EN 1044:
AG 304 |
Brazing joints with temperature stress up to 150 °C
Gap soldering
|
Steel
Stainless steel
Copper
Copper alloys
Nickel
Nickel alloys
|
SFP 89
SFP 891
Flux "S"
|
Oxyfuel torch brazing
Furnace brazing
Induction brazing
ABA-FAG-process
|
Tensils strength of2 the brazing joint |
about
410 N/mm2 |
Melting range |
595 – 630 °C |
Brazing temperature |
610 °C |
|
|
Silver brazing solder 6252 |
Physico-
chemical Data |
Type of
brazing alloy |
Area of brazing |
Base metal |
Flux |
Brazing process |
Welding alloy composition |
Ag: 24 – 26 %
Cu: 39 – 41 %
Sn: 1,5 – 2,5 %
Zn: 31 – 35 % |
DIN 8513:
L-Ag25Sn
EN 1044:
AG 108 |
Brazing joints with temperature stress up to 200 °C
|
Steel
Stainless steel
Copper
Copper alloys
Nickel
Nickel alloys
|
V87
KMB-S 62
SFP 89
SFP 891
Flux "S"
|
Oxyfuel torch brazing
Furnace brazing
Induction brazing
Laser brazing
ABA-FAG-process
|
Tensils strength of2 the brazing joint |
about
360 N/mm2 |
Melting range |
680 – 760 °C |
Brazing temperature |
750 °C |
|
|
Silver brazing solder 6452 |
Physico-
chemical Data |
Type of
brazing alloy |
Area of brazing |
Base metal |
Flux |
Brazing process |
Welding alloy composition |
Ag: 44 – 46 %
Cu: 26 – 28 %
Sn: 2 – 3 %
Zn: 23,5 – 27,5 %
|
DIN 8513:
L-Ag45Sn
EN 1044:
AG 104 |
Brazing joints with temperature stress up to 200 °C
|
Steel
Stainless steel
Copper
Copper alloys
Nickel
Nickel alloys
|
SFP 89
SFP 891
Flux "S"
|
Oxyfuel torch brazing
Furnace brazing
Induction brazing
ABA-FAG-process
|
Tensils strength of2 the brazing joint |
about
350 N/mm2 |
Melting range |
640 – 680 °C |
Brazing temperature |
670 °C |
|
|
Silver brazing solder 6552 |
Physico-
chemical Data |
Type of
brazing alloy |
Area of brazing |
Base metal |
Flux |
Brazing process |
Welding alloy composition |
Ag: 54 – 56 %
Cu: 20 – 22 %
Sn: 1,5 – 2,5 %
Zn: 20 – 24 % |
DIN 8513:
L-Ag55Sn
EN 1044:
AG 103 |
Brazing joints with analogous colour on 18/8 steel
Gap soldering
Qualified in the food industrie
|
Steel
Stainless steel
Copper
Copper alloys
Nickel
Nickel alloys
|
SFP 89
SFP 891
Flux "S"
|
Oxyfuel torch brazing
Furnace brazing
Induction brazing
ABA-FAG-process
|
Tensils strength of2 the brazing joint |
about
350 N/mm2 |
Melting range |
620 – 660 °C |
Brazing temperature |
650 °C |
|
|
Silver brass solder 79 |
Physico-
chemical Data |
Type of
brazing alloy |
Area of brazing |
Base metal |
Flux |
Brazing process |
Welding alloy composition |
Cu: 54 – 56 %
Ag: 4 – 6 %
Si: 0,05 – 0,25 %
Zn: 38 – 42 % |
DIN 8513:
L-Ag5
EN 1044:
AG 208 |
Gap soldering/Braze welding
Weld brazing
Light and thin fluid reccomended in particular for base metals extremly
endangered by
solder brittle.
|
Steel
Low-alloy steel
Malleable iron
Nickel
Copper
|
KMB-S 62
V 87
Oktol 88
Flux "S"
|
Oxyfuel torch brazing
Gas fusion welding
Furnace brazing
ABA-FAG-process
|
Tensils strength of2 the brazing joint |
about
350 N/mm2 |
Melting range |
820 – 870 °C |
Brazing temperature |
860 °C |
|