Heavy metal soldering fluxes


Flux VA 356
Flux 389
Flux 3600 (COM)
Flux 3601 (COM)
Flux 3603 (COM)
Flux 3703 (COM)
Flux 3702 COS
Packaging units

Flux VA 356
Flux typ Soldering temperature Area of soldering
Properties
Base metal Filler metal Soldering process
DIN 8511:
F-SW 11

DIN EN 29454-1:
3.2.2.

150 – 400 °C Particulary suitable for soldering stainless steel.

Very reliable and efficient results.

Residues strongly corrosive - must be removed.
Steel

Stainless steel

Copper

Copper alloys
For stainless steel tin-silver-solders

For other base metals tin-lead-solders
Oxyfuel torch brazing

Furnace brazing

Induction brazing process
top
Flux 389
Flux typ Soldering temperature Area of soldering
Properties
Base metal Filler metal Soldering process
DIN 8511:
F-SW 12

DIN EN 29454-1:
3.1.1.

180 – 450 °C Universal flux for normal soldering performances with tin-lead solders.

Very reliable and efficient results.

Residues strongly corrosive - must be removed.
Steel

Copper

Copper alloys
Tin-lead-solders Oxyfuel torch brazing

Furnace brazing

Induction brazing process
top
Flux 3600 (COM)
Flux typ Soldering temperature Anwendungsgebiete
Eigenschaften
Base metal Filler metal Soldering process
DIN 8511:
F-SW 12


DIN EN 29454-1:
3.1.1.
250 – 500 °C Flux for soldering copper and brass radiators.

Residues strongly corrosive - must be removed.
Copper

Copper alloys
Tin-lead-solders Oxyfuel torch brazing

Furnace brazing

Induction brazing process
top
Flux 3601 (COM)
Flux typ Soldering temperature Area of soldering
Properties
Base metal Filler metal Soldering process
DIN 8511:
F-SW 12


DIN EN 29454-1:
3.1.1.
250 – 500 °C Flux for soldering copper and brass radiators.

Residues strongly corrosive - must be removed.
Copper

Copper alloys
Tin-lead-solders Oxyfuel torch brazing

Furnace brazing

Induction brazing process
top
Flux 3603 (COM)
Flux typ Soldering temperature Area of soldering
Properties
Base metal Filler metal Soldering process
  250 – 500 °C In case of optimal soldering conditions removal of residues is only necessary when special risks of corrosion are existing
Copper

Copper alloys
Tin-lead-solders Oxyfuel torch brazing

Furnace brazing

Induction brazing process
top
Flux 3703 (COM)
Flux typ Soldering temperature Area of soldering
Properties
Base metal Filler metal Soldering process
  250 – 500 °C In case of optimal soldering conditions removal of residues is only necessary when special risks of corrosion are existing Copper

Copper alloys
Tin-lead-solders Oxyfuel torch brazing

Furnace brazing

Induction brazing process
top
Flux 3702 COS
Flux typ Soldering temperature Area of soldering
Properties
Base metal Filler metal Soldering process
  250 – 500 °C Flux used in the production of starter batteries. Lead Lead Welding, founding